    Performance of Multiple Corrosion Protection Systems for Reinforced Concrete Bridge Decks

    Thumbnail
    View/Open
    OReilly_ku_0099D_11287_DATA_1.pdf (19.30Mb)
    Issue Date
    2011-01-18
    Author
    O’Reilly, Matthew
    Publisher
    University of Kansas
    Format
    534 pages
    Type
    Dissertation
    Degree Level
    Ph.D.
    Discipline
    Civil, Environmental, & Architectural Engineering
    Rights
    This item is protected by copyright and unless otherwise specified the copyright of this thesis/dissertation is held by the author.
    Metadata
    Show full item record
    Abstract
    The performance of corrosion protection systems for reinforcing steel in concrete is evaluated. In addition to conventional and conventional epoxy-coated reinforcement, the corrosion protection systems tested include epoxy coatings with improved adhesion to the underlying steel, conventional and conventional epoxy-coated reinforcement used in conjunction with concrete containing one of three corrosion inhibitors, DCI-S, Rheocrete 222+, or Hycrete, epoxy-coated reinforcement with a microencapsulated calcium nitrite primer, multiple-coated reinforcement with a layer of zinc between the epoxy and steel, and pickled 2205 duplex stainless steel. The systems are evaluated using bench-scale and field tests. Two bridges in Kansas, cast with 2205 stainless steel, are monitored using corrosion potential mapping. Epoxy-coated and multiple-coated bars are evaluated to determine the effect of corrosion loss and time on the disbondment of the epoxy coating. Conventional, galvanized, and epoxy-coated reinforcement are evaluated using impressed current to determine the corrosion loss required to crack concrete for each system. A finite element model is developed to represent general and localized corrosion, and the results are used to develop a relationship between concrete cover, bar diameter, and area of bar corroding, and the corrosion loss required to crack concrete. An analysis of pore solutions expressed from cement pastes containing corrosion inhibitors is performed, with pH and selected ion concentrations measured from solutions collected one and seven days after casting. The results obtained from bench-scale and field test specimens are used to estimate cost effectiveness for each system under a 75-year service life. The results show epoxy coatings significantly reduce the corrosion rate compared to conventional reinforcement. Corrosion inhibitors significantly reduce corrosion rates in uncracked concrete. In cracked concrete, corrosion inhibitors also reduce corrosion rates, but their relative effectiveness is reduced. Specimens containing Hycrete exhibit the lowest corrosion rates; however, field specimens containing Hycrete also show signs of scaling. Epoxies with improved adhesion exhibit no improvement over conventional epoxy-coated reinforcement in terms of corrosion rate or disbondment of the epoxy coating. Multiple-coated reinforcement exhibits significantly less disbondment than epoxy-coated reinforcement. Pickled 2205 reinforcement exhibits the least corrosion among all systems tested. Testing of conventional and galvanized reinforcement indicates galvanized reinforcement requires more than twice as much corrosion loss to crack the surrounding concrete compared to conventional reinforcement. An analysis of pore solution extracted from cement pastes containing inhibitors indicates an elevated sulfate content in pore solution collected from specimens containing Hycrete. Increased sulfate levels may explain the reduced strength and critical chloride corrosion threshold observed in concrete containing Hycrete. Elevated sulfate levels are also observed in pore solutions collected 7 days after casting from cement paste containing Rheocrete. An economic analysis of a 0.216-m (8.5-in.) thick bridge deck over a 75-year design life indicates that corrosion protection systems using either coated or stainless steel reinforcement are significantly more cost-effective than any of the systems containing conventional reinforcement..
    URI
    http://hdl.handle.net/1808/7633
    Collections
    • Engineering Dissertations and Theses [1055]
    • Dissertations [4472]

    Items in KU ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.


    We want to hear from you! Please share your stories about how Open Access to this item benefits YOU.


    Contact KU ScholarWorks
    785-864-8983
    KU Libraries
    1425 Jayhawk Blvd
    Lawrence, KS 66045
    785-864-8983

    KU Libraries
    1425 Jayhawk Blvd
    Lawrence, KS 66045
    Image Credits
     

     

    Browse

    All of KU ScholarWorksCommunities & CollectionsThis Collection

    My Account

    LoginRegister

    Statistics

    View Usage Statistics

    Contact KU ScholarWorks
    785-864-8983
    KU Libraries
    1425 Jayhawk Blvd
    Lawrence, KS 66045
    785-864-8983

    KU Libraries
    1425 Jayhawk Blvd
    Lawrence, KS 66045
    Image Credits
     

     

    The University of Kansas
      Contact KU ScholarWorks
    Lawrence, KS | Maps
     
    • Academics
    • Admission
    • Alumni
    • Athletics
    • Campuses
    • Giving
    • Jobs

    The University of Kansas prohibits discrimination on the basis of race, color, ethnicity, religion, sex, national origin, age, ancestry, disability, status as a veteran, sexual orientation, marital status, parental status, gender identity, gender expression and genetic information in the University’s programs and activities. The following person has been designated to handle inquiries regarding the non-discrimination policies: Director of the Office of Institutional Opportunity and Access, IOA@ku.edu, 1246 W. Campus Road, Room 153A, Lawrence, KS, 66045, (785)864-6414, 711 TTY.

     Contact KU
    Lawrence, KS | Maps